Development of a Cissus quadrangularis-Doped Extracellular Matrix and a Hyaluronic Acid-Incorporated Scaffold for Periodontal Regeneration: An In Vitro Study.

PURPOSE: The study aimed to analyze whether adding Cissus quadrangularis (CQ) extract and the extracellular matrix of ovine tendon (TENDON) increases the regenerative potential of mesenchymal stem cells produced in hyaluronic acid (HA) scaffolds for tenogenesis.

MATERIALS AND METHODS: Fifty grams of powdered CQ was mixed with 250 mL of ethanol to prepare the extract. Two grams of hyaluronic acid powder was added to 100 mL of distilled water to make the HA solution. The ovine tendon was decellularized using a mixture of 10% phosphate-buffered saline (PBS), sodium dodecyl sulfate (SDS), and Triton-X. The hydrogel samples were prepared by mixing the extracellular matrix of tendon, HA, and CQ, after which they were divided into study groups such as HA, HA + CQ, HA + TENDON, and HA + CQ + TENDON. Scanning electron microscopy (SEM) analysis, swelling analysis, differentiation analysis, compression test, compatibility assay, and tenogenesis assay were later conducted.

RESULTS: The morphology of the samples was analyzed using SEM. Low levels of swelling of the hydrogels were observed. Cells were found to be viable and showed good differentiation and tenogenesis. Optimal compression levels were observed, and the properties of the prepared hydrogels were satisfactory.

CONCLUSION: The results suggest that the addition of CQ considerably increases the tenogenic potential of the extracellular matrix/HA scaffold. Hence, it can be used as a regenerative material for periodontal tissue regeneration.