3D Printing of TPU-Liquid Metal Composite Inks for the Preparation of Flexible Sensing Electronics.

Direct 3D printing of liquid metal is difficult to form and easy to destroy. In this paper, we developed a 3D printed composite material consisting of a thermoplastic polyurethane (TPU) matrix and liquid metal (LM) dispersed droplets, and introduced the method for realizing 3D printed devices with this composite material: First, the LM is added to 10~50wt %TPU at 190~200 °C through ultrasonic blending to prepare blended ink. After solid cooling, the LM-TPU composite fiber with a diameter of 600 μm was prepared by Wellzoom desktop extruder at 190 °C at an extrusion speed of 400 mm/min. It has excellent elasticity, with a tensile limit of 0.637 N/m2 , and the TPU could evenly wrap LM droplets. Finally, the LM-TPU fiber is 3D printed at 240 °C by using a 3D printer, and 2D/3D flexible electronic devices with heating and conductive functions could be prepared. The microcircuit has good electrical conductivity; after adding voltage, the circuit has heat release; it could be used as heating equipment to keep warm and used in various flexible wearable electronic products.