Effect of Sterilization and Irrigating Solutions on Nanostructure Alteration of Ni-Ti Rotary Instruments in Endodontics: An Atomic Force Microscopic Study.

AIM: This study aimed to evaluate the effect of 5.25% sodium hypochlorite (NaOCl) and 17% ethylenediaminetetraacetic acid (EDTA) and sterilization on the nanostructural alteration of nickel titanium (Ni-Ti) rotary file systems in endodontics using the atomic force microscopy (AFM).

MATERIALS AND METHODS: The study was performed on four commercially available rotary Ni-Ti files: group I-Vortex Blue (Dentsply), group II-ProTaper Next (Dentsply), group III-Mtwo (VDW), and group IV-iRaCe (FKG). Each group was divided into four subgroups ( n = 4), that is, subgroup A-control (new rotary file), subgroup B-subjected for five cycles of autoclave, subgroup C-immersed in 5.25% NaOCl for 5 minutes, and subgroup D-immersed in 17% EDTA solutions for 5 minutes. All the specimens were evaluated with AFM using roughness average (RA) and root-mean-square (RMS) values for surface roughness.

RESULTS: Among control groups, Vortex Blue showed the least RA and RMS values; the highest surface roughness was seen with Mtwo files. All the Ni-Ti rotary files showed a statistically significant ( P <0.05) increase in surface hardness when subjected to autoclave and treatment with different irrigating solutions. In particular, 17% EDTA caused the highest surface deterioration in all the groups.

CONCLUSION: AFM analysis revealed increased surface roughness values recorded for all the rotary files when treated with irrigating solutions and autoclave cycles.