Nanostructured gellan and xanthan hydrogel depot integrated within a baghdadite scaffold augments bone regeneration.

Controlled delivery of biological cues through synthetic scaffolds to enhance the healing capacity of bone defects is yet to be realized clinically. The purpose of this study was development of a bioactive tissue-engineered scaffold providing the sustained delivery of an osteoinductive drug, dexamethasone disodium phosphate (DXP), encapsulated within chitosan nanoparticles (CN). Porous baghdadite (BD; Ca3 ZrSi2 O9 ) scaffolds, a zirconia-modified calcium silicate ceramic, was coated with DXP-encapsulated CN nanoparticles (DXP-CN) using nanostructured gellan and xanthan hydrogel (GX). Crosslinker and GX polymer concentrations were optimized to achieve a homogeneous distribution of hydrogel coating within BD scaffolds. Dynamic laser scattering indicated an average size of 521 ± 21 nm for the DXP-CN nanoparticles. In vitro drug-release studies demonstrated that the developed DXP-CN-GX hydrogel-coated BD scaffolds (DXP-CN-GX-BD) resulted in a sustained delivery of DXP over the 5 days (78 ± 6% of drug release) compared with burst release over 1 h, seen from free DXP loaded in uncoated BD scaffolds (92 ± 8% release in 1 h). To estimate the influence of controlled delivery of DXP from the developed scaffolds, the effect on MG 63 cells was evaluated using various bone differentiation assays. Cell culture within DXP-CN-GX-BD scaffolds demonstrated a significant increase in the expression of early and late osteogenic markers of alkaline phosphatase activity, collagen type 1 and osteocalcin, compared to the uncoated BD scaffold. The results suggest that the DXP-releasing nanostructured hydrogel integrated within the BD scaffold caused sustained release of DXP, improving the potential for osteogenic differentiation. Copyright © 2015 John Wiley & Sons, Ltd.