Compressive strength and fluoride release profile of a glass ionomer cement reinforced with silver-hydroxyapatite-silica hybrid nanoparticles: An in vitro study.

OBJECTIVES: This study aimed to prepare a glass ionomer (GI) cement reinforced with silver-hydroxyapatite-silica (Ag/HA/Si) hybrid nanoparticles and assess its compressive strength and fluoride release profile.

MATERIAL AND METHODS: In this in vitro, experimental study, 60 cylindrical specimens were fabricated with 4mm diameter and 6mm height in 6 groups (n=10) using BracePaste composite, GC Fuji II LC pure RMGI, and RMGI reinforced with 0.1wt%, 0.5wt%, 1wt%, and 2wt% Ag/HA/Si hybrid nanoparticles. The specimens were subjected to compressive force in a universal testing machine to measure their compressive strength (MPa). To assess their fluoride release profile, discs with 3mm diameter and 2mm thickness were fabricated from Fuji II LC pure resin-modified glass ionomer (RMGI), and RMGI with 0.1wt%, 0.5wt%, 1wt%, and 2wt% hybrid nanoparticles, and the concentration of released fluoride was measured by a digital ion-selective electrode. Data were analysed by ANOVA and Scheffe test (alpha=0.05).

RESULTS: The compressive strength was 114.14MPa for BracePaste composite, and 97.14, 97.84, 100.65, 109.5, and 89.33MPa for GI groups with 0%, 0.1%, 0.5%, 1% and 2% hybrid nanoparticles, respectively, with no significant difference among them (P=0.665). Addition of 1% (0.21±0.07μg/mL, P=0.029) and 2% (0.45±0.22μg/mL, P=0.000) hybrid nanoparticles to RMGI significantly increased the amount of released fluoride, compared with the control group (0.09±0.03μg/mL).

CONCLUSIONS: Addition of Ag/HA/Si hybrid nanoparticles to RMGI in the tested concentrations had no significant effect on its compressive strength but addition of 1wt% and 2wt% concentrations of Ag/HA/Si hybrid nanoparticles increased its fluoride release potential.