TEMPO-Oxidized Nanocellulose Films Modified by Tea Saponin Derived from Camellia oleifera : Physicochemical, Mechanical, and Antibacterial Properties.

Nanocellulose materials have been widely used in biomedicine, food packaging, aerospace, composite material, and other fields. In this work, cellulose obtained from Camellia shells through alkali boiling and subbleaching was micro-dissolved and regenerated using the DMAc ( N , N -Dimethylacetamide)/LiCl system, and TOCNs (TEMPO-oxidized cellulose nanofibers) with different degrees of oxidation. The membrane was prepared by filtration of polytetrafluoroethylene (pore size 0.1 μm), and the oxidized nanocellulose film was obtained after drying, Then, the crystallinity, mechanical properties and oxygen barrier properties of the TOCN film were investigated. Furthermore, based on TS (tea saponin) from Camellia oleifera seed cake and TOCNs, TS-TOCN film was prepared by the heterogeneous reaction. The TS-TOCN film not only shows excellent oxygen barrier properties (the oxygen permeability is 2.88 cc·m-2 ·d-1 ) but also has good antibacterial effects on both Gram-negative and Gram-positive bacteria. The antibacterial property is comparable to ZnO-TOCN with the same antibacterial content prepared by the in-situ deposition method. Antioxidant activity tests in vitro showed that TS-TOCN had a significant scavenging effect on DPPH (2,2-Diphenyl-1-picrylhydrazyl) radicals. This design strategy makes it possible for inexpensive and abundant Camellia oleifera remainders to be widely used in the field of biobased materials.