Regioisomeric Spirobifluorene CANAL Ladder Polymers and Their Gas Separation Performance.

We synthesized and characterized two isomeric microporous hydrocarbon ladder polymers from catalytic arene norbornene annulation (CANAL) of regioisomeric bis-norbornene fused spirobifluorenes, where the ladder chains are connected either through the same fluorene unit or across two different fluorene units in spirobifluorene. This pair of isomeric polymers was used to investigate the effect of ladder macromolecular structures on the microporosity and transport properties. Both polymers form mechanically intact films with thermal stability up to 480 °C and relatively high BET surface areas. The polymer formed from 2,7-dibromospirobifluorene showed higher BET surface area and higher gas permeability than the polymer from 2,2'-dibromospirobifluorene despite similar intersegmental spacing as indicated by X-ray scattering. The aging behavior for both polymers followed the same trend as the previously reported CANAL-fluorene polymers, with dramatically increased permselectivities over time, resulting in gas separation performance above the 2008 upper bounds for H2 /CH4 and O2 /N2 .