Effect of different core design made of computer-aided design/computer-aided manufacturing system and veneering technique on the fracture resistance of zirconia crowns: A laboratory study.

Background: It is unclear how the different core designs made of computer-aided design/computer-aided manufacturing (CAD/CAM) system and veneering techniques affect the fracture resistance of endodontically treated teeth.

Aim: The aim of this in vitro study is to investigate the effect of different core designs made of CAD/CAM system and veneering techniques on the fracture resistance of zirconia ceramic crowns.

Materials and Methods: Two types of zirconia copings were designed; the first one with circumferential 0.5-mm chamfer and the second one with circumferential 1-mm deep chamfer. The core specimens (in subgroups) were veneered anatomically with either a layering technique (hand-layer) or with press-on technique resulting in four test groups ( n = 12). All crowns were then cemented using self-adhesive resin cement. After that, all specimens were loaded in a universal testing machine until fractured.

Statistical Analysis: Data were then analyzed with two-way analysis of variance (ANOVA) (α =0.05).

Results: Mean (standard deviation) failure loads for groups ranged from 2412.7 N (±624.6) to 3020.1 N (±1099.8). Two-way ANOVA revealed no statistically significant differences among groups ( P > 0.05). Almost all groups showed cohesive failure in the veneering ceramic.

Conclusions: Within the limitations of this laboratory study, neither the core design nor the veneering technique affected the fracture resistance of all-ceramic crowns significantly.