Framework disorder and its effect on selective hysteretic sorption of a T-shaped azole-based metal-organic framework.

Metal-organic frameworks with highly ordered porosity have been studied extensively. In this paper, the effect of framework (pore) disorder on the gas sorption of azole-based isoreticular Cu(II) MOFs with rtl topology and characteristic 1D tubular pore channels is investigated for the first time. In contrast to other isoreticular rtl metal-organic frameworks, the Cu(II) metal-organic framework based on 5-(1 H -imidazol-1-yl)isophthalate acid has a crystallographically identifiable disordered framework without open N-donor sites. The framework provides a unique example for investigating the effect of pore disorder on gas sorption that can be systematically evaluated. It exhibits remarkable temperature-dependent hysteretic CO2 sorption up to room temperature, and shows selectivity of CO2 over H2 , CH4 and N2 at ambient temperature. The unique property of the framework is its disordered structure featuring distorted 1D tubular channels and DMF-guest-remediated defects. The results imply that structural disorder (defects) may play an important role in the modification of the performance of the material.