Antibacterial-Anti-Inflammatory-Bone Restoration Procedure Achieved by MIN-Loaded PLGA Microsphere for Efficient Treatment of Periodontitis.

The main development process of periodontitis involves periodontal pathogenic bacteria as the initiating factor causing the onset of destructive inflammation, which in turn stimulates the destruction of periodontal tissue. It is difficult to achieve the eradication of periodontitis due to the complex interaction among antibacterial, anti-inflammatory, and bone restoration. Herein, we propose an antibacterial-anti-inflammatory-bone restoration procedural treatment strategy with minocycline (MIN) for the efficient treatment of periodontitis. In brief, MIN was prepared into PLGA microspheres with tunable release behavior using different species of PLGA, respectively. The optimally selected PLGA microspheres (LA:GA with 50:50, 10 kDa, and carboxyl group) had a drug loading of 16.91%, an in vitro release of approximately 30 days, which also had a particle size of approximately 11.8 µm with a smooth appearance and a rounded morphology. The DSC and XRD results showed that the MIN was completely encapsulated in the microspheres as an amorphous state. Cytotoxicity tests demonstrated the safety and biocompatibility of the microspheres (cell viabilities at a concentration of 1-200 μg/mL were greater than 97%), and in vitro bacterial inhibition tests showed that the selected microspheres could achieve effective bacterial inhibition at the initial stage after administration. The favorable anti-inflammatory (low TNF-α and IL-10 levels) and bone restoration effects (BV/TV: 71.8869%; BMD: 0.9782 g/cm3 ; TB.Th: 0.1366 mm; Tb.N: 6.9318 mm-1 ; Tb.Sp: 0.0735 mm) were achieved in a SD rat periodontitis model after administering once a week for four weeks. The MIN-loaded PLGA microspheres were proved to be an efficient and safe treatment for periodontitis by procedural antibacterial, anti-inflammatory, and bone restoration.