Color Stability of Microhybrid and Nanofilled Composite Resins: Effect of Surface Sealant Agents Containing Different Filler Content.
Journal of Contemporary Dental Practice 2019 September 2
AIM: To evaluate the effect of surface sealants containing different filler content on the color stability of microhybrid and nanofilled composite resins.
MATERIALS AND METHODS: The materials evaluated as study groups were comprised a nanofilled composite resin (Filtek Ultimate, 3M ESPE) and a microhybrid composite resin (Filtek Z250, 3M ESPE). Forty-five disc-shaped specimens (10 mm × 2 mm) were prepared from each composite resin. Each study group was divided into three subgroups: control, G-Coat Plus, and Fortify Plus ( n = 15). The baseline color values ( L * a * b *) of each specimen were measured using a spectrophotometer according to the CIE L * a * b * color scale. Then, the specimens were immersed in red wine for a period of 3 hours per day for 15 days (3 hours/day × 15 days). After the immersion period, the color values ( L * a * b *) of each specimen were measured again. The Δ L *, Δ a *, and Δ b * values and the color change value (Δ E ) were calculated. The data were statistically analyzed with two-way ANOVA and Duncan tests ( p = 0.05).
RESULTS: All the composite resin groups demonstrated/indicated much more color changes after immersion in red wine (Δ E > 3.3). The greater Δ E values were observed with the groups applied surface sealants than the control groups ( p < 0.05). Fortify Plus further increased the Δ E values of both composite resins than G Coat Plus ( p < 0.05). Filtek Ultimate showed higher Δ E values than Filtek Z250 in all the subgroups ( p < 0.05).
CONCLUSION: The surface sealants regardless of the filler content negatively influenced the color change of the composite resins after immersed in red wine. The microhybrid composite resin had better color stability than the nanofilled composite resin.
CLINICAL SIGNIFICANCE: There is no favorable effect of using surface sealants on composite resins to prevent discoloration; besides, the sealants can also increase the color alteration.
MATERIALS AND METHODS: The materials evaluated as study groups were comprised a nanofilled composite resin (Filtek Ultimate, 3M ESPE) and a microhybrid composite resin (Filtek Z250, 3M ESPE). Forty-five disc-shaped specimens (10 mm × 2 mm) were prepared from each composite resin. Each study group was divided into three subgroups: control, G-Coat Plus, and Fortify Plus ( n = 15). The baseline color values ( L * a * b *) of each specimen were measured using a spectrophotometer according to the CIE L * a * b * color scale. Then, the specimens were immersed in red wine for a period of 3 hours per day for 15 days (3 hours/day × 15 days). After the immersion period, the color values ( L * a * b *) of each specimen were measured again. The Δ L *, Δ a *, and Δ b * values and the color change value (Δ E ) were calculated. The data were statistically analyzed with two-way ANOVA and Duncan tests ( p = 0.05).
RESULTS: All the composite resin groups demonstrated/indicated much more color changes after immersion in red wine (Δ E > 3.3). The greater Δ E values were observed with the groups applied surface sealants than the control groups ( p < 0.05). Fortify Plus further increased the Δ E values of both composite resins than G Coat Plus ( p < 0.05). Filtek Ultimate showed higher Δ E values than Filtek Z250 in all the subgroups ( p < 0.05).
CONCLUSION: The surface sealants regardless of the filler content negatively influenced the color change of the composite resins after immersed in red wine. The microhybrid composite resin had better color stability than the nanofilled composite resin.
CLINICAL SIGNIFICANCE: There is no favorable effect of using surface sealants on composite resins to prevent discoloration; besides, the sealants can also increase the color alteration.
Full text links
Related Resources
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices 
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app