CAD-CAM milled versus pressed lithium-disilicate monolithic crowns adhesively cemented after distinct surface treatments: Fatigue performance and ceramic surface characteristics.
To evaluate the fatigue failure load (FFL), number of cycles for failure (CFF) and survival probabilities of lithium-disilicate (LD) monolithic crowns manufactured by two processing techniques (pressing vs. CAD/CAM) adhesively cemented to a dentin-analogue material, considering two surface treatments (conventional vs. simplified). Surface characteristics (topography, roughness and fractal dimensions) were also assessed. Forty (40) monolithic crowns were manufactured considering two specific processing techniques for each ceramic system: LDCAD - CAD/CAM lithium-disilicate (IPS e.max CAD, Ivoclar Vivadent); LDPRESS - pressed lithium-disilicate (IPS e.max Press, Ivoclar Vivadent). The crowns were adhesively cemented (Multilink Automix System, Ivoclar Vivadent) onto dentin analogue preparations considering two distinct protocols of surface treatments (conventional - hydrofluoric acid etching + silane application [HF+Sil] or simplified - etching with one-step primer (Monobond Etch&Prime, Ivoclar Vivadent) [EP]). The cemented assembly was stored in distilled water at 37 °C for 3 days and fatigue tests were run (step-stress approach: load ranging from 400 to 2000 N, step-size of 100 N, 15,000 cycles/step, 20 Hz). Fractography, surface topography, roughness, and fractal dimension analyses were performed. LDPRESS [EP] group depicted higher FFL, CFF and survival probabilities in comparison to LDCAD groups, regardless of the conditioning method. A tendency of higher Weibull modulus (mechanical reliability) was observed when using [EP] for both LDPRESS and LDCAD . SEM and AFM analysis showed very distinct initial surface patterns for the distinct processing techniques considered (LDCAD with higher fractal dimension and lower roughness than LDPRESS ), and both surface treatments distinctly affected these surface characteristics. All failures were radial cracks originating at the ceramic-cement interface. Pressed lithium-disilicate monolithic crowns showed better fatigue performance in comparison to CAD/CAM milled crowns, especially when they were treated with self-etching ceramic primer. The surface treatment with self-etching primer led to similar fatigue performance when compared to hydrofluoric acid plus silane application for the same processing technique, but it tended to provide higher mechanical reliability.
Full text links
Related Resources
Trending Papers
Heart failure with preserved ejection fraction: diagnosis, risk assessment, and treatment.Clinical Research in Cardiology : Official Journal of the German Cardiac Society 2024 April 12
Proximal versus distal diuretics in congestive heart failure.Nephrology, Dialysis, Transplantation 2024 Februrary 30
Efficacy and safety of pharmacotherapy in chronic insomnia: A review of clinical guidelines and case reports.Mental Health Clinician 2023 October
World Health Organization and International Consensus Classification of eosinophilic disorders: 2024 update on diagnosis, risk stratification, and management.American Journal of Hematology 2024 March 30
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app