Giant UV Photoresponse of GaN-based photodetectors by surface modification using Phenol functionalized Porphyrin organic molecules.

Organic molecular monolayers (MoLs) have been used for improving the performance of various electronic device structures. In this work, the concept of organic molecular surface modification is applied for improving the performance of GaN-based Metal-Semiconductor-Metal (MSM) Ultraviolet (UV) Photodetectors (PDs). Organic molecules of phenol-functionalized-metallated-Porphyrin (Zn-TPPOH) were adsorbed on GaN and Ni/Zn-TPPOH/GaN/Zn-TPPOH/Ni PD structures were fabricated. This process was beneficial in two ways, firstly the reverse bias dark current was reduced by ~1000 times and secondly, the photocurrent was enhanced by ~100 times, in comparison to the dark and photo current values obtained for Ni/GaN/Ni MSM PDs, at high voltages of 10V. The Responsivity of the devices was increased from 0.22 kA/W to 4.14 kA/W at 5 µW/cm2 optical power density at -10 V bias and at other voltages also. In addition to this, other PD parameters such as Photo-to-dark current ratio and UV-to-Visible rejection ratio were also enhanced. The spectral selectivity of the PDs was improved, which means that the molecularly modified devices became more responsive to UV spectral region and lesser responsive to visible spectral region, in comparison to bare-GaN based devices. Photoluminescence measurements, Power-dependent photocurrent characteristics and Time-resolved photocurrent measurements revealed that the MoL was passivating the defect-related states on GaN. In addition, Kelvin Probe Force Microscopy showed that the MoL was also playing with the surface charge (due to surface states) on GaN, leading to increased Schottky barrier height in dark conditions. Resultant to both these phenomena, the reverse bias dark current was reduced for metal/MoL/GaN/MoL/metal PD structures. Further, the unusual photoconductive gain in the molecularly modified devices has been attributed to Schottky-barrier lowering for UV-illuminated conditions, leading to enhanced photocurrent.