Effect of different surface treatment on the shear bond strength of metal brackets to bleached and desensitized enamel.

INTRODUCTION: The aim of this study was to determine the effect of bleaching and desensitizing on shear bond strength (SBS) of metal brackets to enamel.

METHODS: One hundred extracted human premolar were randomly assigned to 5 groups of 20. In the first group (control), no bleaching or desensitizing agent was used. Groups 2 to 5 were bleached with 37.5% hydrogen peroxide and desensitized with 6.0% potassium nitrate. Surface treatment comprised of etching for 15seconds in groups 1, 2 and 3, Er:yag laser irradiation and etching in group 4 and sandblasting and etching in group 5. Premolar brackets were bonded with Transbond XT and cured for 20seconds and the SBS was tested using a universal testing machine. Adhesive remnant index (ARI) score was used to record the mode of bond failure.

RESULTS: No significant difference was found between the mean SBS (MPa) in groups 1(15.22), 4(14.02), and 5(12.62). SBS in group 4 was significantly higher than group 2 (8.15) (P<0.001). Also, SBS in groups 2 (P<0.001) and 3(11.74) (P=0.012) were significantly lower than group 1. An increased frequency of ARI score of 2 and 3 was observed in groups 1, 4 and 5.

CONCLUSIONS: Bleaching plus desensitizing significantly decreased the SBS of orthodontic brackets. Delaying the bonding procedure for at least 2 weeks or alternative surface treatment methods such as combined laser and acid etching or combined sand blasting and acid etching can improve the SBS.