Microstructural Evolution of Post-Processed Hastelloy X Alloy Fabricated by Laser Powder Bed Fusion.

Materials 2019 Februrary 6
Hastelloy X (HX) is a Ni-based superalloy which is employed to produce gas turbine and gas-cooled reactor sectors due to its outstanding oxidation resistance and high tensile strength at high temperatures. This alloy can be processed by laser powder bed fusion (LPBF) fabricating complex geometries in a single step. However, post-processing thermal treatments must be applied to generate a suitable microstructure for high-temperature applications. The investigation reports the microstructure evolution of LPBF HX samples under specific post-processing treatments. A hot isostatic pressing (HIP) treatment can close the internal cracks and reduce the residual porosity (less than 0.1%). Moreover, the HIP-triggered recrystallization generated equiaxed grains, while the slow cooling rate generated a film of intergranular carbides (Mo-rich M₆C and Cr-rich M23 C₆) and intragranular carbides (Mo-rich M₆C carbides). Therefore, a solution annealing was performed to dissolve the film of carbides which may reduce the ductility. The post solution annealed material consisted of equiaxed grains with ASTM grain size number mainly 4.5-5.5 and inter/intragranular Mo-rich M₆C carbides. The microstructure is highly comparable with solution annealed wrought HX alloy. Finally, after simulating short thermal exposure at 745 °C for 6 h, a significant formation of Cr-rich M23 C₆ carbides was observed strengthening the LPBF HX alloy.

Full text links

We have located links that may give you full text access.
Can't access the paper?
Try logging in through your university/institutional subscription. For a smoother one-click institutional access experience, please use our mobile app.

For the best experience, use the Read mobile app

Mobile app image

Get seemless 1-tap access through your institution/university

For the best experience, use the Read mobile app

All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.

By using this service, you agree to our terms of use and privacy policy.

Your Privacy Choices Toggle icon

You can now claim free CME credits for this literature searchClaim now

Get seemless 1-tap access through your institution/university

For the best experience, use the Read mobile app