Influence of UV irradiation and cold atmospheric pressure plasma on zirconia surfaces: an in vitro study.
International Journal of Oral & Maxillofacial Implants 2018 December 6
PURPOSE: To compare the influence of ultraviolet (UV) irradiation and cold atmospheric pressure plasma (CAP) treatment on surface structure, surface chemistry, cytocompatibility, and cell behavior on zirconia in vitro.
MATERIALS AND METHODS: Zirconia samples (TZ-3YSBE) were treated by UV irradiation, oxygen plasma, or argon plasma for 12 minutes each and compared with the nontreated samples. Surface analysis was conducted using scanning electron microscopy, roughness analysis, and x-ray photoelectron spectroscopy. Cell proliferation, viability, and cell attachment as well as cytotoxicity were evaluated using MC3T3-E1 murine osteoblasts cultivated directly on the zirconia samples.
RESULTS: Surface structure and roughness were not affected by the surface treatments. CAP and UV irradiation significantly reduced organic material and increased the surface oxidation on the zirconia samples. Furthermore, CAP and UV treatment significantly decreased the contact angle on the zirconia samples, indicating superhydrophilicity. Cell attachment was significantly increased on oxygen plasma-treated zirconia samples compared with the nontreated samples at all times (P < .001). After 24 and 48 hours, cell proliferation and viability (P < .001) were significantly increased on oxygen plasma-treated samples in comparison with the nontreated, UV-treated, and argon plasma-treated samples. Neither UV nor CAP treatment led to cytotoxicity.
CONCLUSION: In vitro, surface treatment by UV irradiation or CAP causes a significant reduction of organic material, increases the hydrophilicity of zirconia, and improves the conditions for osteoblasts. Results stipulate that treatment of zirconia surfaces with oxygen plasma may favor cell proliferation.
MATERIALS AND METHODS: Zirconia samples (TZ-3YSBE) were treated by UV irradiation, oxygen plasma, or argon plasma for 12 minutes each and compared with the nontreated samples. Surface analysis was conducted using scanning electron microscopy, roughness analysis, and x-ray photoelectron spectroscopy. Cell proliferation, viability, and cell attachment as well as cytotoxicity were evaluated using MC3T3-E1 murine osteoblasts cultivated directly on the zirconia samples.
RESULTS: Surface structure and roughness were not affected by the surface treatments. CAP and UV irradiation significantly reduced organic material and increased the surface oxidation on the zirconia samples. Furthermore, CAP and UV treatment significantly decreased the contact angle on the zirconia samples, indicating superhydrophilicity. Cell attachment was significantly increased on oxygen plasma-treated zirconia samples compared with the nontreated samples at all times (P < .001). After 24 and 48 hours, cell proliferation and viability (P < .001) were significantly increased on oxygen plasma-treated samples in comparison with the nontreated, UV-treated, and argon plasma-treated samples. Neither UV nor CAP treatment led to cytotoxicity.
CONCLUSION: In vitro, surface treatment by UV irradiation or CAP causes a significant reduction of organic material, increases the hydrophilicity of zirconia, and improves the conditions for osteoblasts. Results stipulate that treatment of zirconia surfaces with oxygen plasma may favor cell proliferation.
Full text links
Related Resources
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app