Evaluation of the Effect of Glow Discharge Plasma Surface Treatment on Bonding Cements to Zirconia.
Background: The major difference in the chemical composition of Y-TZP ceramics, as compared with conventional porcelain, led researchers to develop alternative solutions for achieving durable and long term bonding with the zirconia surface.
Objective: The study aims to evaluate the effects of glow discharge treatment on the bonding between cement and zirconia.
Methods: The zirconia rings and rods were prepared with the Zirconia Y-TZP powder and TZ-3YSB-E (Tosoh-Zirconia) through auto-mix to investigate the glow discharge and thermo-cycling. An orientation Teflon mold was used to centralize each rod into the zirconia ring, and aided as a cementation jig during the cementation procedure.
Results: Cohesive failure (2/3 or more of luting agent remained on the zirconia surface) has been majorly observed with RelyX Ultimate, while adhesion failure (less than 1/3 of the luting agent remained on the zirconia surface) has been primarily observed in Ketac-Cem. Mixed failure was observed among the three specimen including Rely X Unicem 2, Multilink Auto-mix and Ceramir.
Conclusion: The glow discharge surface treatment procedure had a major impact on bond strength to zirconia.
Objective: The study aims to evaluate the effects of glow discharge treatment on the bonding between cement and zirconia.
Methods: The zirconia rings and rods were prepared with the Zirconia Y-TZP powder and TZ-3YSB-E (Tosoh-Zirconia) through auto-mix to investigate the glow discharge and thermo-cycling. An orientation Teflon mold was used to centralize each rod into the zirconia ring, and aided as a cementation jig during the cementation procedure.
Results: Cohesive failure (2/3 or more of luting agent remained on the zirconia surface) has been majorly observed with RelyX Ultimate, while adhesion failure (less than 1/3 of the luting agent remained on the zirconia surface) has been primarily observed in Ketac-Cem. Mixed failure was observed among the three specimen including Rely X Unicem 2, Multilink Auto-mix and Ceramir.
Conclusion: The glow discharge surface treatment procedure had a major impact on bond strength to zirconia.
Full text links
Related Resources
Trending Papers
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app