The Effect of Casein Phosphopeptide-Amorf Calcium Phosphate and Acidulated Phosphate Fluoride Gel on Dental Erosion in Primary Teeth: An in Vitro Study.

OBJECTIVE: This study aimed to investigate the effect of acidulated phosphate fluoride (APF) gel and casein phosphopeptide/amorphous calciumphosphate (CPP-ACP) on the dental erosion produced by carbonated soft drink in primary teeth.

STUDY DESIGN: This study evaluated by an in vitro model the effect of APF gel and CPP-ACP on the dental enamel previously subjected to erosive challenge with carbonated soft drink. Sixty sound human primary molars were prepared by embedding the crown sections in acrylic resin blocks leaving the enamel surfaces exposed. The surface roughness of the enamel was measured with prophilometry at baseline. Specimens were randomly divided into three treatment groups (n:20): artificial saliva, CPP-ACP, 1.23% APF gel. All specimens were then exposed to an erosive challenge of carbonated soft drink and artificial saliva for 20 cycles of 20 seconds each. Demineralization-remineralization cycles was repeated twice at eight-hour intervals and roughness values were measured. Enamel samples were treated with artificial saliva, CPP-ACP, 1.23% APF gel applied for 10 min after erosive challenge. The arithmetic average roughness (Ra) readings were recorded after remineralization agents were applied.

RESULTS: The mean surface roughness in all groups increased significantly after erosion process and decreased after remineralization treatment. After treatment, the mean surface roughness of the 1.23% APF gel group was significantly less than the other groups and the mean surface roughness of the artificial saliva group was significantly more than the other groups. 1.23% APF gel showed the highest protective effect against erosive enamel loss.

CONCLUSIONS: Under the conditions of this study, artificial saliva, CPP-ACP and 1.23% APF treatments were able to reduce erosive enamel loss produced by carbonated soft drink in primary teeth. However, 1.23% APF gel showed the highest protective effect against erosive enamel loss.