A resonance frequency analysis of sandblasted and acid-etched implants with different diameters: a prospective clinical study during the initial healing period.

PURPOSE: The possibility of immediate or early loading has become popular in implant dentistry. A prerequisite for the immediate or early loading of an implant prosthesis is the achievement of initial stability in the implant. Moreover, in response to clinicians' interest in verifying clinical stability to determine the optimal time point for functional loading, a non-invasive method to assess implant stability has been developed on the basis of resonance frequency analysis (RFA). The primary objective of this study was to monitor the stability of sandblasted, large-grit, and acid-etched (SLA) implants with different diameters during the early phases of healing by RFA. The secondary objective was to evaluate how the initial stability of implants varied depending on different surface modifications and other contributing factors.

METHODS: Thirty-five implants (25 SLA implants and 10 resorbable blasting media [RBM] implants) placed in 20 subjects were included. To measure implant stability, RFA was performed at baseline and at 1, 2, 3, 4, 6, and 10 weeks after surgery.

RESULTS: The longitudinal changes in the implant stability quotient (ISQ) values were similar for the SLA implants with different diameters and for the RBM implants. During the initial healing period, the ISQ decreased after installation and reached its lowest values at 1 week and 2 weeks, respectively. The mean ISQ values in the SLA implants were significantly higher in Ø 5.0 mm implants than in Ø 4.0 mm implants. Men showed a higher ISQ than women. Mandibular sites showed a higher ISQ than maxillary sites.

CONCLUSIONS: All implants used in this study are suitable for immediate or early loading under appropriate indications. A wider diameter and SLA surface treatment of implants could improve the stability, if the implant is fixed with at least 30 Ncm of insertion torque.