The reinforcement effect of polyethylene fibre and composite impregnated glass fibre on fracture resistance of endodontically treated teeth: An in vitro study
AIM: The aim of this study was to evaluate the fracture resistance of endodontically treated maxillary premolars with wide mesio-occluso-distal (MOD) cavities restored with either composite resin, or composite resin reinforced with different types of fibres.
MATERIALS AND METHODS: Fifty human maxillary premolars were selected. Five intact teeth served as positive controls. Endodontic therapy was carried out in the remaining forty-five teeth. Standardized MOD cavities were prepared in all the teeth. The teeth were restored with a nanocomposite using an incremental technique. These forty five teeth were randomly divided into three experimental groups (Group A, B and C) (n = 15). The teeth in Group A did not undergo any further procedures. The teeth in Group B and C were reinforced with composite impregnated glass fibre and polyethylene fibre, respectively. Fracture resistance was measured in Newtons (N).
RESULTS: The positive controls showed the highest mean fracture resistance (811.90 N), followed by Group B (600.49N), Group A (516.96N) and Group C (514.64N), respectively. One Way analysis of variance (ANOVA) test revealed a statistically significant difference between all the groups (P = 0.001). Post-hoc Tukey test revealed a moderately significant difference (P = 0.034) between Control and Group B, and a strongly significant difference between Control and Group A (P = 0.002), and Control and Group C (P = 0.001).
CONCLUSIONS: Endodontic therapy and MOD cavity preparation significantly reduced the fracture resistance of endodontically treated maxillary premolars (P = 0.001). No statistically significant difference was found between the experimental groups (Group A, B and C) (P > 0.1). However, the fracture resistance of the composite impregnated glass fibre reinforced group was much higher than the others.