Ultrafast electron-phonon coupling in hollow gold nanospheres.
Physical Chemistry Chemical Physics : PCCP 2011 December 29
Electronic energy relaxation in hollow gold nanospheres (HGNs) was studied using femtosecond time-resolved transient absorption spectroscopy. A range of HGNs having outer diameter-to-shell thickness aspect ratios of 3.5 to 9.5 were synthesized by a galvanic replacement method. The HGNs exhibited electron-phonon relaxation times that decreased from 1.18 ± 0.16 to 0.59 ± 0.08 ps as the aspect ratio increased over this range. The corresponding electron-phonon coupling constants, G, ranged from (1.67 ± 0.22) to (3.33 ± 0.45) × 10(16) W m(-3) K(-1). Electron-phonon coupling was also determined for solid gold nanospheres (SGNs) with diameters spanning 20 nm to 83 nm; no size dependence was observed for these structures. The HGNs with high aspect ratios exhibited larger electron-phonon coupling constants than the SGNs, whose average G value was (1.9 ± 0.2) × 10(16) W m(-3) K(-1). By comparison, low-aspect ratio HGNs exhibited values comparable to SGNs. The electron-phonon coupling of high-aspect ratio HGNs was also influenced by the surrounding fluid dielectric; slightly smaller G values were obtained when methanol was the solvent as opposed to water. This coupling enhancement observed for high-aspect ratio HGNs was attributed to the large surface to volume ratio of these structures, which results in non-negligible contributions from the environment.
Full text links
Related Resources
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app