Alteration of shell nacre micromorphology in blue mussel Mytilus edulis after exposure to free-ionic silver and silver nanoparticles.

This study describes the morphology of inner shell surface (ISS) of the blue mussel Mytilus edulis Linnaeus after short-term exposures to radiolabeled silver in free-ionic ((110m)Ag(+)) and engineered nanoparticulate ((110m)AgNPs, <40 nm) phases. Radiolabeled silver in starting solutions was used in a similar low concentration (∼15 Bq mL(-1)) for both treatments. After exposure experiments radiolabeled silver was leached from the ISS using HCl. It concentration for shells from both treatments was ∼0.5 Bq mL(-1). Whole ISS of young individuals and prismatic layer of adults showed no evidence of any major alteration process after silver uptake. However, the nacre portion of adult mussels exposed to both treatments revealed distinct doughnut shape structures (DSS) formed by calcium carbonate micrograins that covered the surface of aragonite tablets. Scanning electron microscope (SEM) imaging revealed the existence of only minor differences in DSS morphology between mussels exposed to Ag(+) and AgNPs. From literature survey, DSS were also found in bivalves exposed to Cd(2+). The DSS occurring in a specimen of a field-collected bivalve is also shown. Formation of distinctive DSS can be explained by a disturbance of the shell calcification mechanism. Although the occurrence of DSS is not exclusively associated with metal bioavailability to the mussels, the morphology of DSS seems to be linked to the speciation of the metal used in the uptake experiments.