Temperature dependence of oxygen reduction activity at Nafion-coated bulk Pt and Pt/carbon black catalysts.
Journal of Physical Chemistry. B 2006 August 25
Oxygen reduction reaction (ORR) activity and H(2)O(2) formation at Nafion-coated film electrodes of bulk-Pt and Pt nanoparticles dispersed on carbon black (Pt/CB) were investigated in 0.1 M HClO(4) solution at 30 to 110 degrees C by using a channel flow double electrode method. We have found that the apparent rate constants k(app) (per real Pt active surface area) for the ORR at bulk-Pt (with and without Nafion-coating) and Nafion-coated Pt/CB (19.3 and 46.7 wt % Pt, d(Pt) = 2.6 to 2.7 nm) thin-film electrodes were in beautiful agreement with each other in the operation conditions of polymer electrolyte fuel cells (PEFCs), i.e., 30-110 degrees C and ca. 0.7 to 0.8 V vs RHE. The H(2)O(2) yield was 0.6-1.0% at 0.7-0.8 V on all Nafion-coated Pt/CB and bulk-Pt and irrespective of Pt-loading level and temperature. Nafion coating was pointed out to be a major factor for the H(2)O(2) formation on Pt catalysts modifying the surface property, because H(2)O(2) production was not detected at the bulk-Pt electrode without Nafion coating.
Full text links
Related Resources
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app