Effects of the frequency and duration of cyclic stress on the mechanical properties of cultured collagen fascicles from the rabbit patellar tendon.

The effects of frequency or duration of cyclic stress on the mechanical properties of collagen fascicles were studied by means of in vitro tissue culture experiments. Collagen fascicles of approximately 300 microm in diameter were obtained from rabbit patellar tendons. During culture, cyclic stress having the peak stress of approximately 2 MPa was applied to the fascicles at 1 Hz for 1 hour/day (1 Hz-1 h group), at 1 Hz for 4 hours/day (1 Hz-4 h group), or at 4 Hz for 1 hour/day (4 Hz-1 h group). The frequency of 4 Hz and the duration of 1 hour/day are considered to be similar to those of the in vivo stress applied to fascicles in the intact rabbit patellar tendon. After culture for 1 or 2 weeks, the mechanical properties of the fascicles were determined using a microtensile tester, and were compared to the properties of non-cultured, fresh fascicles (control group) and the fascicles cultured under no load condition (non-loaded group). The tangent modulus and tensile strength of fascicles in the 4 Hz-1 h group were similar to those in the control group; however, the fascicles of the 1 Hz-1 h and 1 Hz-4 h groups had significantly lower values than those of the control group. There was no significant difference in the tensile strength between the 1 Hz-1 h and non-loaded groups, although the strength in the 1 Hz-4 h group was significantly higher than that of the non-loaded group. It was concluded that the frequency and duration of cyclic stress significantly affect the mechanical properties of cultured collagen fascicles. If we apply cyclic stress having the frequency and duration which are experienced in vivo, the biomechanical properties are maintained at control, normal level. Lower frequencies or less cycles of applied force induce adverse effects.

Full text links

We have located links that may give you full text access.
Can't access the paper?
Try logging in through your university/institutional subscription. For a smoother one-click institutional access experience, please use our mobile app.

For the best experience, use the Read mobile app

Mobile app image

Get seemless 1-tap access through your institution/university

For the best experience, use the Read mobile app

All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.

By using this service, you agree to our terms of use and privacy policy.

Your Privacy Choices Toggle icon

You can now claim free CME credits for this literature searchClaim now

Get seemless 1-tap access through your institution/university

For the best experience, use the Read mobile app