The influence of plasma arc vs. halogen standard or soft-start irradiation on polymerization shrinkage kinetics of polymer matrix composites.

OBJECTIVES: To determine polymerization shrinkage kinetics and hardness of photo-activated polymer matrix composites (PMC) after plasma arc vs. halogen standard or soft-start irradiation.

METHODS: Polymerization shrinkage was measured using the 'deflecting disk technique', and Knoop hardness was measured at the bottom of 1.5 mm thick specimens stored for 24 h at 37 degrees C. The materials comprised one micro-filled (Silux Plus) and four fine hybrid PMC (Definite, Herculite XRV, Solitaire 2 and Z250). The irradiation protocols included halogen standard irradiation at three intensities (TriLight, ESPE), ramp curing (dito), step curing (HiLight, ESPE), pulse polymerization (VIP Light, BISCO) and plasma curing (Apollo 95E, DMDS; PAC Light, ADT).

RESULTS: Standard halogen irradiation at reduced intensity delayed the start and slowed down the progression of shrinkage strain, but (except for Z250) as well produced lower hardness. Soft-start halogen curing produced similar kinetics but maintained hardness. Plasma arc irradiation resulted in an immediate start and a rapid progression of polymerization contraction, but produced low hardness values in Definite (cured by the ADT unit) and in Solitaire 2 (both units). Z250 featured the highest, Silux Plus the lowest maximum rate of contraction. Despite soft-start irradiation, contraction of Z250 progressed faster than that of Silux Plus with halogen standard irradiation at high intensity.

CONCLUSIONS: Soft-start halogen irradiation protocols provide better chances for compensation of shrinkage stress by flow within PMC without compromising hardness and may contribute to a better marginal integrity of the restorations. Irradiation protocols should be individually adjusted to compensate for the different curing characteristics of PMC.

Full text links

We have located links that may give you full text access.
Can't access the paper?
Try logging in through your university/institutional subscription. For a smoother one-click institutional access experience, please use our mobile app.

For the best experience, use the Read mobile app

Mobile app image

Get seemless 1-tap access through your institution/university

For the best experience, use the Read mobile app

All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.

By using this service, you agree to our terms of use and privacy policy.

Your Privacy Choices Toggle icon

You can now claim free CME credits for this literature searchClaim now

Get seemless 1-tap access through your institution/university

For the best experience, use the Read mobile app